1、基础处理：采用打磨机对浮物，凹凸不平的地面进行深度打 磨，清理灰尘杂物，如果凹入太深的区域用中涂层材料加石英砂修补，找平，固化后再进行底涂层施工； 1, basic processing: using grinding machine's, uneven ground deep grinding, cleaning dust sundry, if sunken into the deep area of quartz sand with coating material in repairing, leveling, the bottom of the reentry after curing coating construction; 2、底涂层：用树脂胶料加适量稀释剂滚涂一遍，增加附着力以及封闭基础地面的潮气，水气，避免基础层与环氧涂层起壳，脱层； 2. Bottom coating: use resin adhesive to add an appropriate amount of diluent to roll over, increase adhesion and seal base ground moisture, water vapor, avoid base layer and epoxy coating shell, remove layer; 3、玻纤布和中涂层施工：先摊铺玻纤布然后刷涂防腐砂浆中涂，每铺一层就在涂刷一道防腐砂浆中涂，直达到玻纤防腐地坪厚度规定的厚度为止； In 3, glass fiber cloth and coating construction: first, paving glass fiber cloth and then brush in the anticorrosive mortar, each spread a layer in the besmear brushs a anticorrosive mortar coating, straight meet the minimum thickness of the glass fiber anticorrosive floor thickness; 4、腻子层：用环氧防腐中涂材料调配石英砂或双飞粉刮批腻子层，按需要施工二至三道，要求达到平整无孔洞、以利面涂施工； 4. Putty layer: use epoxy anticorrosive materials to prepare quartz sand or double-fly powder to scrape the putty layer and build two to three as needed to achieve the smooth and no holes and the construction of the surface. 5 防腐面涂层：用防腐面漆树脂胶料或色漆涂布二道；注：所用树脂依设计而定，涂刮完毕后用带齿滚洞消泡； 5. Anti-corrosion surface coating: using anticorrosive paint resin or colored paint coating; Note: the resin is designed according to the design. After finishing, it is used to remove the cavity with teeth. 6、在玻纤防腐地坪施工过程中，注意材料调配的比例，还有搅拌材料的手法和搅拌的时间，避免防腐材料在加入助剂时产生化学反应出现大量气泡，增加施工难度，还要花大量的时间用带齿滚洞消泡，还有一种情况就是，在搅拌材料时不均匀，涂刷后才产生气泡，待固化就会影面层的表面效果； 6, in the process of fiberglass anticorrosive floor construction, pay attention to material mixing ratio, and technique of mixing materials and mixing time, avoid corrosion materials react when it joined agents appear a large number of air bubbles, increase the construction difficulty, also spend a lot of time using a toothed roll foam, there is also a situation is, uneven when mixing materials, besmear to brush after the bubble, for curing will film surface of the surface effect;